- 熔体流动速率 [g/10min]: 5.0
- 密度 [g/cm3]: 0.935
- 拉伸强度 [MPa]: 16.0
- 脆化温度 [℃]: -75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.935 g/cc | 0.0338 lb/in³ | ASTM D1505 |
| ESCR 100% Igepal® | >= 150 hour | >= 150 hour | F50; ASTM D1693B |
| Melt Flow | 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 5.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 66 | 66 | ASTM D2240 |
| Tensile Strength at Break | 17.0 MPa | 2470 psi | ASTM D638 |
| Tensile Strength, Yield | 16.0 MPa | 2320 psi | ASTM D638 |
| Elongation at Break | 590 % | 590 % | ASTM D638 |
| Flexural Strength | 13.0 MPa | 1890 psi | ASTM D790 |
| 1% Secant Modulus | 420 MPa | 60900 psi | ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 114 °C | 237 °F | ASTM D1525 |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | ASTM D746 |