- 熔体流动速率 [g/10min]: 1.0
- 脆化温度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.919 g/cc | 0.919 g/cc | ASTM D1505 |
| Environmental Stress Crack Resistance | >= 1000 hour @Temperature 50.0 °C | >= 1000 hour @Temperature 122 °F | F50, 25% Igepal; ASTM D1639 |
| Thickness | 38.0 microns | 1.50 mil | |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 12.0 MPa | 1740 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 14.0 MPa | 2030 psi | ASTM D882 |
| Film Elongation at Break, MD | 1000 % | 1000 % | ASTM D882 |
| Film Elongation at Break, TD | 1200 % | 1200 % | ASTM D882 |
| Secant Modulus, MD | 0.260 GPa | 37.7 ksi | ASTM D882 |
| Secant Modulus, TD | 0.270 GPa | 39.2 ksi | ASTM D882 |
| Elmendorf Tear Strength, MD | 5.71 g/micron | 145 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 14.6 g/micron | 370 g/mil | ASTM D1922 |
| Dart Drop | 3.40 g/micron | 86.4 g/mil | ASTM D1709 |
| Dart drop Test | 130 g | 0.287 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 37.0 MPa | 5370 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 34.0 MPa | 4930 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 122 °C | 252 °F | ASTM D2117 |
| Vicat Softening Point | 102 °C | 216 °F | ASTM D1525 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 |
| Optical Properties | Metric | English | Comments |
| Haze | 15 % | 15 % | ASTM D1003 |
| Gloss | 53 % | 53 % | ASTM D2457 |