- 熔体流动速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.928
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.928 g/cc | 0.0335 lb/in³ | ISO 1183 |
| Thickness | 40.0 microns | 1.57 mil | |
| Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.30 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 300 % | 300 % | ISO 527-3 |
| Film Elongation at Break, TD | 550 % | 550 % | ISO 527-3 |
| Secant Modulus, MD | 0.290 GPa | 42.1 ksi | ASTM D882-A |
| Secant Modulus, TD | 0.300 GPa | 43.5 ksi | ASTM D882-A |
| Impact | 71.4 | 71.4 | Puncture Resistance, force (N); ASTM D5748 |
| Puncture Energy | 3.20 J | 2.36 ft-lb | ASTM D5748 |
| Coefficient of Friction, Dynamic | 0.50 | 0.50 | ISO 8295 |
| Tear Strength, Total | 2.10 N | 0.472 lb (f) | TD; ISO 6383/2 |
| 2.40 N | 0.540 lb (f) | MD; ISO 6383/2 | |
| Dart Drop | 2.50 g/micron | 63.5 g/mil | ISO 7765/1 |
| Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | >= 117 °C | >= 243 °F | ISO 11357/03 |
| Vicat Softening Point | 106 °C | 223 °F | A (10N); ISO 306 |
| Optical Properties | Metric | English | Comments |
| Haze | 6.0 % | 6.0 % | ASTM D1003 |
| Gloss | 100 % | 100 % | ASTM D2457 |
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified |