- 熔体流动速率 [g/10min]: 0.9
- 密度 [g/cm3]: 0.923
- 拉伸强度 [MPa]: 13.28
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.923 g/cc | 0.0333 lb/in³ | LE 4421; ASTM D792 |
| 1.05 g/cc | 0.0379 lb/in³ | LE 4432; ASTM D792 | |
| Melt Flow | 0.90 g/10 min | 0.90 g/10 min | LE 4421; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | >= 13.28 MPa | >= 1926 psi | Heat Aging (7 days at 121°C); ASTM D412 |
| 14.8 MPa | 2140 psi | ASTM D412 | |
| Elongation at Break | <= 50 % | <= 50 % | Hot Creep Test (150°C, .2 MPa); ICEA T-28-562 |
| 270 % | 270 % | Heat Aging (7 days at 121°C); ASTM D412 | |
| 300 % | 300 % | ASTM D412 | |
| Tensile Set | <= 5.0 % | <= 5.0 % | Hot Creep Test (150°C,.2 MPa); ICE T-28-562 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.3 @Frequency 60 Hz | 2.3 @Frequency 60 Hz | ASTM D150 |
| Dielectric Strength | >= 21.7 kV/mm | >= 550 kV/in | ASTM D149 |
| Dissipation Factor | 0.00050 @Frequency 60 Hz | 0.00050 @Frequency 60 Hz | ASTM D150 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | >= 171 °C | >= 340 °F | |
| Front Barrel Temperature | >= 146 °C | >= 295 °F | |
| Die Temperature | >= 177 °C | >= 350 °F | |
| Head Temperature | >= 177 °C | >= 351 °F | |