- 熔体流动速率 [g/10min]: 0.75
- 密度 [g/cm3]: 0.927
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.927 g/cc | 0.0335 lb/in³ | ISO 1183 |
| Thickness | 40.0 microns | 1.57 mil | |
| Melt Flow | 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.75 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 300 % | 300 % | ISO 527-3 |
| Film Elongation at Break, TD | 600 % | 600 % | ISO 527-3 |
| Secant Modulus, MD | 0.250 GPa | 36.3 ksi | ASTM D882-A |
| Secant Modulus, TD | 0.270 GPa | 39.2 ksi | ASTM D882-A |
| Impact | 62.7 | 62.7 | Puncture Resistance, force (N); ASTM D5748 |
| Puncture Energy | 2.40 J | 1.77 ft-lb | ASTM D5748 |
| Coefficient of Friction, Dynamic | 0.50 | 0.50 | ISO 8295 |
| Tear Strength, Total | 2.00 N | 0.450 lb (f) | TD; ISO 6383/2 |
| 3.00 N | 0.674 lb (f) | MD; ISO 6383/2 | |
| Dart Drop | 2.50 g/micron | 63.5 g/mil | ISO 7765/1 |
| Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | >= 115 °C | >= 239 °F | ISO 11357/03 |
| Vicat Softening Point | 101 °C | 214 °F | A (10N); ISO 306 |
| Optical Properties | Metric | English | Comments |
| Haze | 7.0 % | 7.0 % | ASTM D1003 |
| Gloss | 100 % | 100 % | ASTM D2457 |
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified |