- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.921
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | ASTM D1505 | ||
| Thickness | 38.0 microns | 1.50 mil | |||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ASTM D638 | ||
| Film Elongation at Break, MD | 287 % | 287 % | ASTM D882 | ||
| Film Elongation at Break, TD | 995 % | 995 % | ASTM D882 | ||
| Elongation at Break | 542 % | 542 % | ASTM D638 | ||
| Coefficient of Friction | 0.43 | 0.43 | ASTM D1894 | ||
| Elmendorf Tear Strength, TD | 4.40 g/micron | 112 g/mil | ASTM D1922 | ||
| Dart Drop | 3.02 g/micron | 76.7 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 35.0 MPa | 5080 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | ASTM D882 | ||
| Heat Seal Strength Initiation Temperature | 105 °C | 221 °F | Sealing Initial Temperature; Braskem® Method | ||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 89.0 °C | 192 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 6.0 % | 6.0 % | ASTM D1003 | ||
| Gloss | 10.5 % | 10.5 % | 60° angle; ASTM D2457 | ||
| Descriptive Properties | |||||
| Minimum Recommended Thickness | 30 µm | ||||