- 熔体流动速率 [g/10min]: 2.5
- 密度 [g/cm3]: 0.923
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.923 g/cc | 0.0333 lb/in³ | ASTM-D792 | ||
| Melt Flow | 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 230 % | 230 % | ASTM-D882 | ||
| Film Elongation at Break, TD | 930 % | 930 % | ASTM-D882 | ||
| Elmendorf Tear Strength TD | 110 g | 110 g | ASTM-D1922 | ||
| Elmendorf Tear Strength, TD | 4.40 g/micron | 112 g/mil | ASTM-D1922 | ||
| Dart Drop | 2.40 g/micron | 61.0 g/mil | ASTM-D1709 | ||
| Dart drop Test | 60.0 g | 0.132 lb | ASTM-D1709 | ||
| Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ASTM-D882 | ||
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | ASTM-D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 6.0 % | 6.0 % | ASTM-D1003 | ||
| Gloss | 110 % | 110 % | Angle 60°; ASTM-D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Blow-up Ratio (BUR) | 1.8 - 3.0 | 1.8 - 3.0 | Blow Film Extrusion | ||
| Descriptive Properties | |||||
| Temperature Profile (°C) | 120-170 | Blow Film Extrusion | |||