- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.918
- 弯曲模量 [MPa]: 0.131
- 脆化温度 [℃]: -75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D1505 |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 15.2 MPa | 2200 psi | Transverse to Flow; ASTM D882 |
| 17.2 MPa | 2490 psi | Direction of Flow; ASTM D882 | |
| Elongation at Break | 300 % | 300 % | Direction of Flow; ASTM D882 |
| 500 % | 500 % | Transverse to Flow; ASTM D882 | |
| Flexural Modulus | 0.131 GPa | 19.0 ksi | MD; ASTM D790 |
| 0.152 GPa | 22.0 ksi | TD; ASTM D790 | |
| Impact | 130 | 130 | g; F50; ASTM D1709 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | ASTM D746 |
| Optical Properties | Metric | English | Comments |
| Haze | 15 % | 15 % | ASTM D1003 |
| Gloss | 35 % | 35 % | 45°; ASTM D2457 |