- 熔体流动速率 [g/10min]: 24.0
- 密度 [g/cm3]: 0.923
- 弯曲模量 [MPa]: 0.303
- 脆化温度 [℃]: -35.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.923 g/cc | 0.0333 lb/in³ | ASTM D1505 |
| Melt Flow | 24 g/10 min @Load 2.16 kg, Temperature 190 °C | 24 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM D882 |
| Elongation at Break | 150 % | 150 % | ASTM D882 |
| Flexural Modulus | 0.303 GPa | 43.9 ksi | chs 0.05 in/min; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -35.0 °C | <= -31.0 °F | ASTM D746 |