- 密度 [g/cm3]: 0.922
- 拉伸强度 [MPa]: 11.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 - 0.924 g/cc | 0.0333 - 0.0334 lb/in³ | ASTM D1505 |
| Thickness | 50.0 microns | 1.97 mil | |
| Melt Index of Compound | 0.10 - 0.14 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.10 - 0.14 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 18.0 MPa | 2610 psi | ASTM D638 |
| Tensile Strength, Yield | 11.0 MPa | 1600 psi | ASTM D638 |
| Film Elongation at Break, MD | 595 % | 595 % | ASTM D882 |
| Film Elongation at Break, TD | 740 % | 740 % | ASTM D882 |
| Elongation at Break | 625 % | 625 % | ASTM D638 |
| Secant Modulus, MD | 0.0920 GPa | 13.3 ksi | 5%; ASTM D882 |
| Secant Modulus, TD | 0.0910 GPa | 13.2 ksi | 5%; ASTM D882 |
| Coefficient of Friction, Dynamic | 0.56 | 0.56 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 8.80 g/micron | 224 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 14.4 g/micron | 366 g/mil | ASTM D1922 |
| Dart drop Test | 395 g | 0.871 lb | (method A); ASTM D1709 |
| Film Tensile Strength at Break, MD | 20.0 MPa | 2900 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 95.0 °C | 203 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 13 % | 13 % | ASTM D1003 |
| Gloss | 62 % | 62 % | @ 60° Gardner; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 180 - 195 °C | 356 - 383 °F | Mixture Zone |
| Feed Temperature | 170 - 185 °C | 338 - 365 °F | |
| Adapter Temperature | 200 - 220 °C | 392 - 428 °F | |
| Blow-up Ratio (BUR) | 3.0 | 3.0 | Recommended |