- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.912
- 透光率 [%]: 97.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.912 g/cc | 0.0329 lb/in³ | ASTM D792 |
| Oxygen Transmission | 282 cc-mm/m²-24hr-atm | 716 cc-mil/100 in²-24hr-atm | ASTM D3985 |
| Thickness | 20.3 microns | 0.800 mil | |
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 9.832 MPa | 1426 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 8.956 MPa | 1299 psi | ASTM D882 |
| Film Elongation at Break, MD | 464 % | 464 % | ASTM D882 |
| Film Elongation at Break, TD | 691 % | 691 % | ASTM D882 |
| Secant Modulus, MD | 0.128 GPa | 18.6 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.144 GPa | 20.9 ksi | 2% Secant; ASTM D882 |
| Impact | 295 | 295 | [ft-lbf/in3]; Puncture Resistance; Dow Method |
| Elmendorf Tear Strength MD | 326 g | 326 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 533 g | 533 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 16.04 g/micron | 407.5 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 26.230 g/micron | 666.25 g/mil | ASTM D1922 |
| Dart drop Test | 449 g | 0.990 lb | Method B; ASTM D1709 |
| Film Tensile Strength at Break, MD | 49.01 MPa | 7108 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 45.26 MPa | 6565 psi | ASTM D882 |
| Heat Seal Strength Initiation Temperature | 95.0 °C | 203 °F | 1 lb/in heat seal strength; 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 123 °C | 253 °F | Dow Method (DSC) |
| Vicat Softening Point | 93.0 °C | 199 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 8.0 % | 8.0 % | ASTM D1003 |
| Gloss | 67 % | 67 % | 45°; ASTM D2457 |
| Transmission, Visible | 97 % | 97 % | Clarity; ASTM D1746 |