- 密度 [g/cm3]: 0.92
- 拉伸强度 [MPa]: 11.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 - 0.926 g/cc | 0.0332 - 0.0335 lb/in³ | ASTM D1505 |
| Thickness | 50.0 microns | 1.97 mil | |
| Melt Index of Compound | 1.8 - 2.6 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.8 - 2.6 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ASTM D638 |
| Tensile Strength, Yield | 11.0 MPa | 1600 psi | ASTM D638 |
| Film Elongation at Break, MD | 365 % | 365 % | ASTM D882 |
| Film Elongation at Break, TD | 670 % | 670 % | ASTM D882 |
| Elongation at Break | 550 % | 550 % | ASTM D638 |
| Secant Modulus, MD | 0.0970 GPa | 14.1 ksi | 5%; ASTM D882 |
| Secant Modulus, TD | 0.105 GPa | 15.2 ksi | 5%; ASTM D882 |
| Coefficient of Friction, Dynamic | 0.12 | 0.12 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 8.40 g/micron | 213 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 5.40 g/micron | 137 g/mil | ASTM D1922 |
| Dart drop Test | 130 g | 0.287 lb | (method A); ASTM D1709 |
| Film Tensile Strength at Break, MD | 20.0 MPa | 2900 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 18.0 MPa | 2610 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 94.0 °C | 201 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 9.0 % | 9.0 % | ASTM D1003 |
| Gloss | 90 % | 90 % | @ 60° Gardner; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 160 - 175 °C | 320 - 347 °F | Plasticizing Zone |
| 165 - 180 °C | 329 - 356 °F | Mixture Zone | |
| Feed Temperature | 150 - 165 °C | 302 - 329 °F | |
| Adapter Temperature | 170 - 180 °C | 338 - 356 °F | |
| Blow-up Ratio (BUR) | 3.0 | 3.0 | Recommended |