Petroquimica Triunfo Trithene® TS 4016 LDPE and LLDPE Blend - Film

Petroquimica Triunfo Trithene® TS 4016 LDPE and LLDPE Blend - Film 物性表: Petroquimica Triunfo Trithene® TS 4016 LDPE and LLDPE Blend - Film物性表及特性介绍,Petroquimica Triunfo Trithene® TS 4016 LDPE and LLDPE Blend - Film注塑参数详情,如需Petroquimica Triunfo Trithene® TS 4016 LDPE and LLDPE Blend - Film下载, 可到相关下载区下载
  • 密度 [g/cm3]: 0.923
 
Physical PropertiesMetricEnglishComments
Density 0.923 g/cc0.0333 lb/in³ASTM D1505
Thickness 50.0 microns1.97 mil
Melt Index of Compound 1.6 g/10 min
@Load 2.16 kg,
Temperature 190 °C
1.6 g/10 min
@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
 
Mechanical PropertiesMetricEnglishComments
Film Elongation at Break, MD 460 %460 %ASTM D882
Film Elongation at Break, TD 780 %780 %ASTM D882
Secant Modulus, MD 0.100 GPa14.5 ksi5%; ASTM D882
Secant Modulus, TD 0.110 GPa16.0 ksi5%; ASTM D882
Coefficient of Friction, Dynamic 0.100.10ASTM D1894
Elmendorf Tear Strength, MD 7.00 g/micron178 g/milASTM D1922
Elmendorf Tear Strength, TD 10.5 g/micron267 g/milASTM D1922
Dart drop Test 160 g0.353 lb(method A); ASTM D1709
Film Tensile Strength at Break, MD 25.0 MPa3630 psiASTM D882
Film Tensile Strength at Break, TD 22.0 MPa3190 psiASTM D882
 
Optical PropertiesMetricEnglishComments
Haze 9.0 %9.0 %ASTM D1003
Gloss 63 %63 %45° - Gardner; ASTM D2457
 96 %96 %@ 60° Gardner; ASTM D2457
 
Processing PropertiesMetricEnglishComments
Processing Temperature 170 - 175 °C338 - 347 °FPlasticizing Zone
 170 - 180 °C338 - 356 °FMixture Zone
Feed Temperature 160 - 165 °C320 - 329 °F
Adapter Temperature 175 - 185 °C347 - 365 °F
 
Descriptive Properties
Proportion LLDPE %22.5PTN-570-Q

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-41127.html

免责声明: 本文 Petroquimica Triunfo Trithene® TS 4016 LDPE and LLDPE Blend - Film 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4