Dow FLEXOMER™ DFDA-1137 NT 7 Very Low Density Polyethylene (VLDPE) Resin

Dow FLEXOMER™ DFDA-1137 NT 7 Very Low Density Polyethylene (VLDPE) Resin 物性表: Dow FLEXOMER™ DFDA-1137 NT 7 Very Low Density Polyethylene (VLDPE) Resin物性表及特性介绍,Dow FLEXOMER™ DFDA-1137 NT 7 Very Low Density Polyethylene (VLDPE) Resin注塑参数详情,如需Dow FLEXOMER™ DFDA-1137 NT 7 Very Low Density Polyethylene (VLDPE) Resin下载, 可到相关下载区下载
  • 密度 [g/cm3]: 0.905
  • 脆化温度 [℃]: -100.0
 
Physical PropertiesMetricEnglishComments
Density 0.905 g/cc0.0327 lb/in³natural resin; ASTM D792
Environmental Stress Crack Resistance >= 500 hour>= 500 hourFo; Compression molded parts prepared according to ASTM D 1928, condition A.; ASTM D1693
Melt Index of Compound 1.0 g/10 min
@Load 2.16 kg,
Temperature 190 °C
1.0 g/10 min
@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
 
Mechanical PropertiesMetricEnglishComments
Hardness, Shore A 9494Compression molded parts prepared according to ASTM D 1928 Procedure C.; ASTM D676
Tensile Strength at Break 19.3 MPa2800 psiCompression molded parts prepared according to ASTM D 1928 Procedure C.; ASTM D638
Elongation at Break 900 %900 %Compression molded parts prepared according to ASTM D 1928 Procedure C.; ASTM D638
1% Secant Modulus 117 MPa17000 psiCompression molded parts prepared according to ASTM D 1928 Procedure C.; ASTM D638
 
Thermal PropertiesMetricEnglishComments
Melting Point 118 °C244 °FDow Method (DSC)
Vicat Softening Point 86.1 °C187 °FASTM D1525
Brittleness Temperature <= -100 °C<= -148 °FCompression molded parts prepared according to ASTM D 1928, procedure A.; ASTM D746

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-41149.html

免责声明: 本文 Dow FLEXOMER™ DFDA-1137 NT 7 Very Low Density Polyethylene (VLDPE) Resin 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4