Dow 650I Low Density Polyethylene Resin

Dow 650I Low Density Polyethylene Resin 物性表: Dow 650I Low Density Polyethylene Resin物性表及特性介绍,Dow 650I Low Density Polyethylene Resin注塑参数详情,如需Dow 650I Low Density Polyethylene Resin下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 2.0
  • 密度 [g/cm3]: 0.928
 
Physical PropertiesMetricEnglishComments
Density 0.928 g/cc0.0335 lb/in³ASTM D792
Thickness 50.8 microns2.00 mil
Melt Flow 2.0 g/10 min
@Load 2.16 kg,
Temperature 190 °C
2.0 g/10 min
@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
 
Mechanical PropertiesMetricEnglishComments
Film Tensile Strength at Yield, MD 14.58 MPa2115 psiASTM D882
Film Tensile Strength at Yield, TD 14.60 MPa2118 psiASTM D882
Film Elongation at Break, MD 606 %606 %ASTM D882
Film Elongation at Break, TD 780 %780 %ASTM D882
Secant Modulus, MD 0.246998 GPa35.8246 ksi2% Secant; ASTM D882
Secant Modulus, TD 0.275128 GPa39.9046 ksi2% Secant; ASTM D882
Impact 3232[ft-lbf/in3]; Puncture Resistance; Dow Method
 25322532[ft-lbf/in3]; Toughness MD; ASTM D882
 26402640[ft-lbf/in3]; Toughness TD; ASTM D882
Elmendorf Tear Strength MD 379 g379 gASTM D1922
Elmendorf Tear Strength TD 449 g449 gASTM D1922
Elmendorf Tear Strength, MD 7.461 g/micron189.5 g/milASTM D1922
Elmendorf Tear Strength, TD 8.839 g/micron224.5 g/milASTM D1922
Dart drop Test 89.0 g0.196 lbMethod A; ASTM D1709
Film Tensile Strength at Break, MD 24.24 MPa3515 psiASTM D882
Film Tensile Strength at Break, TD 21.04 MPa3051 psiASTM D882
 
Optical PropertiesMetricEnglishComments
Haze 7.2 %7.2 %ASTM D1003
Gloss 77 %77 %45°; ASTM D2457

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-41158.html

免责声明: 本文 Dow 650I Low Density Polyethylene Resin 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4