- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.911
- 透光率 [%]: 98.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.911 g/cc | 0.0329 lb/in³ | ASTM D792 |
| Thickness | 20.3 microns | 0.800 mil | |
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 9.65 MPa | 1400 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 9.65 MPa | 1400 psi | ASTM D882 |
| Film Elongation at Break, MD | 570 % | 570 % | ASTM D882 |
| Film Elongation at Break, TD | 930 % | 930 % | ASTM D882 |
| Secant Modulus, MD | 0.161337 GPa | 23.4004 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.17099 GPa | 24.800 ksi | 2% Secant; ASTM D882 |
| Impact | 325 | 325 | [ft-lbf/in3]; Puncture Resistance; Dow Method |
| 2700 | 2700 | [ft-lbf/in3]; Toughness MD; ASTM D882 | |
| 4200 | 4200 | [ft-lbf/in3]; Toughness TD; ASTM D882 | |
| Elmendorf Tear Strength MD | 400 g | 400 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 500 g | 500 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 19.7 g/micron | 500 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 24.6 g/micron | 625 g/mil | ASTM D1922 |
| Dart drop Test | 170 g | 0.375 lb | Method B; ASTM D1709 |
| Film Tensile Strength at Break, MD | 51.7 MPa | 7500 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 49.6 MPa | 7200 psi | ASTM D882 |
| Heat Seal Strength Initiation Temperature | 90.0 °C | 194 °F | 1 lb/in heat seal strength; 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 122 °C | 252 °F | Dow Method (DSC) |
| Vicat Softening Point | 94.0 °C | 201 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 9.8 % | 9.8 % | ASTM D1003 |
| Gloss | 58 % | 58 % | 45°; ASTM D2457 |
| Transmission, Visible | 98 % | 98 % | Clarity; ASTM D1746 |