- 熔体流动速率 [g/10min]: 2.3
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D792 |
| Thickness | 50.8 microns | 2.00 mil | |
| Melt Flow | 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.3 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 11.64 MPa | 1688 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 11.02 MPa | 1598 psi | ASTM D882 |
| Film Elongation at Break, MD | 451 % | 451 % | ASTM D882 |
| Film Elongation at Break, TD | 620 % | 620 % | ASTM D882 |
| Secant Modulus, MD | 0.166233 GPa | 24.1104 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.208084 GPa | 30.1805 ksi | 2% Secant; ASTM D882 |
| Impact | 43 | 43 | [ft-lbf/in3]; Puncture Resistance; Dow Method |
| 1695 | 1695 | [ft-lbf/in3]; Toughness MD; ASTM D882 | |
| 1790 | 1790 | [ft-lbf/in3]; Toughness TD; ASTM D882 | |
| Elmendorf Tear Strength MD | 321 g | 321 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 189 g | 189 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 6.319 g/micron | 160.5 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 3.72 g/micron | 94.5 g/mil | ASTM D1922 |
| Dart drop Test | 96.0 g | 0.212 lb | Method A; ASTM D1709 |
| Film Tensile Strength at Break, MD | 21.75 MPa | 3155 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 19.62 MPa | 2845 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 108 °C | 226 °F | Dow Method (DSC) |
| Vicat Softening Point | 92.0 °C | 198 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 16.1 % | 16.1 % | ASTM D1003 |
| Gloss | 40 % | 40 % | 45°; ASTM D2457 |