- 熔体流动速率 [g/10min]: 0.88
- 密度 [g/cm3]: 0.9239
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.9239 g/cc | 0.03338 lb/in³ | ASTM D792 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 0.88 g/10 min | 0.88 g/10 min | ASTM D1238 |
| Antiblock Level | 1245 ppm | 1245 ppm | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 11.9 MPa | 1730 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 12.3 MPa | 1780 psi | ASTM D882 |
| Film Elongation at Break, MD | 273 % | 273 % | ASTM D882 |
| Film Elongation at Break, TD | 543 % | 543 % | ASTM D882 |
| Secant Modulus, MD | 0.196963 GPa | 28.5674 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.224997 GPa | 32.6335 ksi | 2% Secant; ASTM D882 |
| Impact | 666 | 666 | [ft-lbf/in3]; Toughness MD; ASTM D882 |
| 770 | 770 | [ft-lbf/in3]; Toughness TD; ASTM D882 | |
| Elmendorf Tear Strength MD | 194 g | 194 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 184 g | 184 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 7.64 g/micron | 194 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 7.24 g/micron | 184 g/mil | ASTM D1922 |
| Dart drop Test | 78.0 g | 0.172 lb | Method A; ASTM D1709 |
| Film Tensile Strength at Break, MD | 25.39 MPa | 3683 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 17.33 MPa | 2513 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 112 °C | 234 °F | Dow Method (DSC) |
| Vicat Softening Point | 97.0 °C | 207 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 6.0 % | 6.0 % | ASTM D1003 |
| Gloss | 71 % | 71 % | 45°; ASTM D2457 |