- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.922
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in³ | |
| Thickness | 40.0 microns | 1.57 mil | |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg | 2.0 g/10 min @Load 4.76 lb | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 11.8 MPa | 1710 psi | |
| Film Tensile Strength at Yield, TD | 11.6 MPa | 1680 psi | |
| Film Elongation at Break, MD | 300 % | 300 % | |
| Film Elongation at Break, TD | 600 % | 600 % | |
| Coefficient of Friction | 0.50 | 0.50 | |
| Elmendorf Tear Strength MD | 300 g | 300 g | |
| Elmendorf Tear Strength TD | 170 g | 170 g | |
| Elmendorf Tear Strength, MD | 7.50 g/micron | 191 g/mil | |
| Elmendorf Tear Strength, TD | 4.30 g/micron | 109 g/mil | |
| Dart Drop | 2.80 g/micron | 71.1 g/mil | |
| Film Tensile Strength at Break, MD | 25.7 MPa | 3730 psi | |
| Film Tensile Strength at Break, TD | 22.2 MPa | 3220 psi | |
| Optical Properties | Metric | English | Comments |
| Haze | 5.4 % | 5.4 % | |
| Gloss | 67 % | 67 % | 45° |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 188 °C | 370 °F | Film extrusion temperature |