- 熔体流动速率 [g/10min]: 1.1
- 密度 [g/cm3]: 0.919
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in³ | ExxonMobil Method | ||
| Thickness | 38.1 microns | 1.50 mil | |||
| Melt Flow | 1.1 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.1 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Antiblock Level | 3000 ppm | 3000 ppm | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 11.0 MPa | 1600 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 10.4 MPa | 1510 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 150 % | 150 % | ASTM D882 | ||
| Film Elongation at Break, TD | 580 % | 580 % | ASTM D882 | ||
| Puncture Energy | 1.08 J | 0.800 ft-lb | ExxonMobil Method | ||
| Elmendorf Tear Strength MD | 340 g | 340 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 70 g | 70 g | ASTM D1922 | ||
| Dart drop Test | 140 g | 0.309 lb | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 29.0 MPa | 4200 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 24.1 MPa | 3500 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 200 MPa | 29000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 255 MPa | 37000 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 107 °C | 225 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 11 % | 11 % | ASTM D1003 | ||
| Gloss | 49 % | 49 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||