- 熔体流动速率 [g/10min]: 3.0
- 密度 [g/cm3]: 0.921
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | ExxonMobil Method | ||
| Thickness | 38.1 microns | 1.50 mil | |||
| Melt Flow | 3.0 g/10 min | 3.0 g/10 min | ExxonMobil Method | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 6.89 MPa | 1000 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 6.21 MPa | 900 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 290 % | 290 % | ASTM D882 | ||
| Film Elongation at Break, TD | 660 % | 660 % | ASTM D882 | ||
| Elmendorf Tear Strength, MD | 7.09 g/micron | 180 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 3.94 g/micron | 100 g/mil | ASTM D1922 | ||
| Dart Drop | 2.36 g/micron | 60.0 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 31.0 MPa | 4500 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 17.9 MPa | 2600 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 145 MPa | 21000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 152 MPa | 22000 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 110 °C | 230 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 3.1 % | 3.1 % | ASTM D1003 | ||
| Gloss | 75 % | 75 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.