- 熔体流动速率 [g/10min]: 2.1
- 密度 [g/cm3]: 0.923
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.923 g/cc | 0.0333 lb/in³ | ExxonMobil Method | ||
| Thickness | 38.1 microns | 1.50 mil | |||
| Melt Flow | 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.1 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Antiblock Level | 2000 ppm | 2000 ppm | |||
| Slip Level | 400 ppm | 400 ppm | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 11.0 MPa | 1600 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 12.4 MPa | 1800 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 130 % | 130 % | ASTM D882 | ||
| Film Elongation at Break, TD | 540 % | 540 % | ASTM D882 | ||
| Puncture Energy | 0.362 J | 0.267 ft-lb | ExxonMobil Method | ||
| Elmendorf Tear Strength MD | 580 g | 580 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 110 g | 110 g | ASTM D1922 | ||
| Dart drop Test | 90.0 g | 0.198 lb | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 26.9 MPa | 3900 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 18.6 MPa | 2700 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 234 MPa | 34000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 296 MPa | 43000 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 112 °C | 233 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 7.3 % | 7.3 % | ASTM D1003 | ||
| Gloss | 65 % | 65 % | 45°; ASTM D2457 | ||
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||