- 密度 [g/cm3]: 0.913
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.913 g/cc | 0.0330 lb/in³ | ASTM D1505 | ||
| Particle Size | >= 150 µm | >= 150 µm | pan, 9% | ||
| <= 400 µm | <= 400 µm | sieve < 5% | |||
| Melt Index of Compound | 70 g/10 min @Load 2.16 kg, Temperature 190 °C | 70 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 41 | 41 | ASTM D2240 | ||
| Elongation at Break | 100 % | 100 % | 50 mm/min; ASTM D638 | ||
| Tensile Modulus | 0.0900 GPa | 13.1 ksi | 1 mm/min; ASTM D638 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 100 °C | 212 °F | DSC; ASTM D3418 | ||
| Vicat Softening Point | 75.0 °C | 167 °F | ASTM D1525 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 200 °C | 392 °F | recommended | ||
| Descriptive Properties | |||||
| Max Dry Flow | max 37 sec/100g | ASTM | |||