- 熔体流动速率 [g/10min]: 0.75
- 密度 [g/cm3]: 0.921
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | TSTM 209 B |
| Melt Flow | 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.75 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Stress | 16.7 MPa | 2420 psi | at Break, MD; ASTM D882 |
| Elongation at Break | >= 300 % | >= 300 % | ASTM D882, MD |
| >= 450 % | >= 450 % | ASTM D882, TD | |
| Dart drop Test | 120 g | 0.265 lb | ASTM D1709 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 94.0 °C | 201 °F | ASTM D1525 |
| Heat Distortion Temperature | 33.0 °C | 91.4 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 180 - 210 °C | 356 - 410 °F | |