- 熔体流动速率 [g/10min]: 4.0
- 密度 [g/cm3]: 0.924
- 拉伸强度 [MPa]: 10.4
- 弯曲模量 [MPa]: 0.291
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | ASTM D792 | ||
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 4.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 10.4 MPa | 1510 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | ASTM D882 | ||
| Tensile Strength, Yield | 10.4 MPa | 1510 psi | ASTM D638 | ||
| Film Elongation at Break, MD | 251 % | 251 % | ASTM D882 | ||
| Film Elongation at Break, TD | 553 % | 553 % | ASTM D882 | ||
| Elongation at Break | 538 % | 538 % | ASTM D638 | ||
| Flexural Modulus | 0.291 GPa | 42.2 ksi | at 1%; ASTM D790 | ||
| Secant Modulus, MD | 0.164 GPa | 23.8 ksi | at 1%; ASTM D882 | ||
| Secant Modulus, TD | 0.195 GPa | 28.3 ksi | at 1%; ASTM D882 | ||
| Impact | 54.9 | 54.9 | J/mm; NOVA Chemicals Puncture test | ||
| Coefficient of Friction | >= 0.60 | >= 0.60 | ASTM D1894 | ||
| Elmendorf Tear Strength, MD | 6.30 g/micron | 160 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 3.30 g/micron | 83.8 g/mil | ASTM D1922 | ||
| Dart Drop | 2.00 g/micron | 50.8 g/mil | F50, ASTM D1709/A | ||
| Film Tensile Strength at Break, MD | 20.5 MPa | 2970 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 16.5 MPa | 2390 psi | ASTM D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 8.6 % | 8.6 % | ASTM D1003 | ||
| Gloss | 54 % | 54 % | at 45°; ASTM D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 170 - 190 °C | 338 - 374 °F | |||
| Descriptive Properties | |||||
| Blow Up Ratio | 2:1 to 3:1 | ||||