- 熔体流动速率 [g/10min]: 0.2
- 密度 [g/cm3]: 0.923
- 缺口冲击强度: 5.3
- 拉伸强度 [MPa]: 17.9
- 断裂伸长率 [%]: 22.8
- 弯曲强度 [MPa]: 21.4
- 弯曲模量 [MPa]: 0.779
- 硬度: 60.0
- 热变形温度 [℃]: 57.0
- 脆化温度 [℃]: -118.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.923 - 1.06 g/cc | 0.0333 - 0.0383 lb/in³ | Average value: 0.954 g/cc Grade Count:21 |
| Moisture Vapor Transmission | 0.410 - 0.410 cc-mm/m²-24hr-atm @Temperature 37.8 - 37.8 °C | 1.04 - 1.04 cc-mil/100 in²-24hr-atm @Temperature 100 - 100 °F | Average value: 0.410 cc-mm/m²-24hr-atm Grade Count:2 |
| 0.410 - 0.410 cc-mm/m²-24hr-atm @Thickness 0.0254 - 0.0254 mm | 1.04 - 1.04 cc-mil/100 in²-24hr-atm @Thickness 0.00100 - 0.00100 in | Average value: 0.410 cc-mm/m²-24hr-atm Grade Count:2 | |
| Environmental Stress Crack Resistance | 30.0 - 1500 hour | 30.0 - 1500 hour | Average value: 671 hour Grade Count:9 |
| Melt Flow | 0.200 - 21.0 g/10 min | 0.200 - 21.0 g/10 min | Average value: 5.24 g/10 min Grade Count:15 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 60.0 - 70.0 | 60.0 - 70.0 | Average value: 65.0 Grade Count:4 |
| Hardness, Shore D | 65.0 - 67.0 | 65.0 - 67.0 | Average value: 65.9 Grade Count:7 |
| Tensile Strength, Ultimate | 21.4 - 30.3 MPa | 3100 - 4390 psi | Average value: 26.2 MPa Grade Count:5 |
| Tensile Strength, Yield | 17.9 - 31.0 MPa | 2600 - 4500 psi | Average value: 25.9 MPa Grade Count:15 |
| Elongation at Break | 500 - 2800 % | 500 - 2800 % | Average value: 823 % Grade Count:13 |
| Flexural Yield Strength | 22.8 - 37.9 MPa | 3310 - 5500 psi | Average value: 29.8 MPa Grade Count:5 |
| Flexural Modulus | 0.779 - 1.55 GPa | 113 - 225 ksi | Average value: 1.18 GPa Grade Count:18 |
| Izod Impact, Notched | 5.30 - 7.50 J/cm | 9.93 - 14.1 ft-lb/in | Average value: 6.57 J/cm Grade Count:3 |
| 4.30 - 5.30 J/cm @Temperature -29.0 - -29.0 °C | 8.06 - 9.93 ft-lb/in @Temperature -20.2 - -20.2 °F | Average value: 4.63 J/cm Grade Count:3 | |
| Gardner Impact | 34.0 - 36.0 J | 25.1 - 26.6 ft-lb | Average value: 34.5 J Grade Count:4 |
| Tensile Impact | 68.3 - 131 J/cm | 128 - 245 ft-lb/in | Average value: 110 J/cm Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 108 - 120 µm/m-°C | 60.0 - 66.7 µin/in-°F | Average value: 116 µm/m-°C Grade Count:3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 57.0 - 92.0 °C | 135 - 198 °F | Average value: 74.1 °C Grade Count:10 |
| Vicat Softening Point | 122 - 134 °C | 252 - 273 °F | Average value: 127 °C Grade Count:5 |
| Brittleness Temperature | -118 - -75.0 °C | -180 - -103 °F | Average value: -87.7 °C Grade Count:9 |