- 熔体流动速率 [g/10min]: 0.025
- 密度 [g/cm3]: 0.924
- 缺口冲击强度: 0.196
- 拉伸强度 [MPa]: 11.0
- 断裂伸长率 [%]: 13.8
- 弯曲强度 [MPa]: 10.0
- 弯曲模量 [MPa]: 0.280
- 硬度: 33.0
- 热变形温度 [℃]: 47.2
- 脆化温度 [℃]: -180.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 - 1.05 g/cc | 0.0334 - 0.0379 lb/in³ | Average value: 0.954 g/cc Grade Count:377 |
| Volatiles | 0.00000900 - 0.100 % | 0.00000900 - 0.100 % | Average value: 0.0667 % Grade Count:3 |
| Apparent Bulk Density | 0.590 - 0.610 g/cc | 0.0213 - 0.0220 lb/in³ | Average value: 0.595 g/cc Grade Count:17 |
| Water Absorption | 0.000 - 0.0700 % | 0.000 - 0.0700 % | Average value: 0.0155 % Grade Count:22 |
| Moisture Absorption at Equilibrium | 0.0100 - 0.0500 % | 0.0100 - 0.0500 % | Average value: 0.0233 % Grade Count:3 |
| Particle Size | 5.00 - 1200 µm | 5.00 - 1200 µm | Average value: 614 µm Grade Count:4 |
| Viscosity | 32000 - 200000 cP @Temperature 190 - 190 °C | 32000 - 200000 cP @Temperature 374 - 374 °F | Average value: 89000 cP Grade Count:7 |
| 32000 - 200000 cP @Shear Rate 300 - 5000 1/s | 32000 - 200000 cP @Shear Rate 300 - 5000 1/s | Average value: 89000 cP Grade Count:7 | |
| Viscosity Measurement | 280 - 460 | 280 - 460 | Average value: 350 Grade Count:5 |
| Environmental Stress Crack Resistance | 1.00 - 3000 hour | 1.00 - 3000 hour | Average value: 182 hour Grade Count:88 |
| 2.00 - 500 hour @Temperature 50.0 - 50.0 °C | 2.00 - 500 hour @Temperature 122 - 122 °F | Average value: 127 hour Grade Count:14 | |
| 2.00 - 10.0 hour @Temperature 50.0 - 50.0 °C | 2.00 - 10.0 hour @Temperature 122 - 122 °F | Average value: 127 hour Grade Count:12 | |
| 2.00 - 10.0 hour @Thickness 1.90 - 2.00 mm | 2.00 - 10.0 hour @Thickness 0.0748 - 0.0787 in | Average value: 127 hour Grade Count:12 | |
| Oxidative Induction Time (OIT) | 20.0 - 100 min | 20.0 - 100 min | Average value: 47.5 min Grade Count:4 |
| Linear Mold Shrinkage | 0.0100 - 0.0300 cm/cm | 0.0100 - 0.0300 in/in | Average value: 0.0204 cm/cm Grade Count:15 |
| Linear Mold Shrinkage, Transverse | 0.0130 - 0.0300 cm/cm | 0.0130 - 0.0300 in/in | Average value: 0.0173 cm/cm Grade Count:3 |
| Melt Flow | 0.0250 - 1610 g/10 min | 0.0250 - 1610 g/10 min | Average value: 28.2 g/10 min Grade Count:356 |
| Base Resin Melt Index | 2.00 - 20.0 g/10 min | 2.00 - 20.0 g/10 min | Average value: 7.00 g/10 min Grade Count:8 |
| Spiral Flow | 15.5 - 53.8 cm | 6.10 - 21.2 in | Average value: 32.3 cm Grade Count:34 |
| Ash | 0.0300 - 0.0500 % | 0.0300 - 0.0500 % | Average value: 0.0433 % Grade Count:3 |
| Collected Volatile Condensable Material | 0.300 - 1.00 % | 0.300 - 1.00 % | Average value: 0.388 % Grade Count:16 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 33.0 - 66.0 | 33.0 - 66.0 | Average value: 48.7 Grade Count:7 |
| Hardness, Shore D | 55.0 - 76.0 | 55.0 - 76.0 | Average value: 64.5 Grade Count:190 |
| Ball Indentation Hardness | 35.0 - 45.0 MPa | 5080 - 6530 psi | Average value: 41.4 MPa Grade Count:9 |
| Tensile Strength, Ultimate | 10.0 - 43.0 MPa | 1450 - 6240 psi | Average value: 21.6 MPa Grade Count:140 |
| Film Tensile Strength at Yield, MD | 21.0 - 35.0 MPa | 3050 - 5080 psi | Average value: 28.9 MPa Grade Count:5 |
| Film Tensile Strength at Yield, TD | 23.0 - 37.5 MPa | 3340 - 5440 psi | Average value: 31.1 MPa Grade Count:5 |
| Tensile Strength, Yield | 11.0 - 43.0 MPa | 1600 - 6240 psi | Average value: 26.3 MPa Grade Count:314 |
| Film Elongation at Break, MD | 595 - 900 % | 595 - 900 % | Average value: 709 % Grade Count:5 |
| Film Elongation at Break, TD | 650 - 950 % | 650 - 950 % | Average value: 860 % Grade Count:5 |
| Elongation at Break | 4.00 - 1900 % | 4.00 - 1900 % | Average value: 543 % Grade Count:271 |
| Elongation at Yield | 6.60 - 80.0 % | 6.60 - 80.0 % | Average value: 11.5 % Grade Count:65 |
| Modulus of Elasticity | 0.565 - 1.50 GPa | 81.9 - 218 ksi | Average value: 0.940 GPa Grade Count:50 |
| Flexural Yield Strength | 13.8 - 48.3 MPa | 2000 - 7000 psi | Average value: 28.1 MPa Grade Count:20 |
| Flexural Modulus | 0.280 - 1.81 GPa | 40.6 - 263 ksi | Average value: 1.10 GPa Grade Count:280 |
| Compressive Yield Strength | 4.00 - 31.7 MPa | 580 - 4600 psi | Average value: 14.2 MPa Grade Count:10 |
| Secant Modulus | 0.750 - 1.54 GPa | 109 - 224 ksi | Average value: 1.06 GPa Grade Count:26 |
| Izod Impact, Notched | 0.196 - 5340 J/cm | 0.367 - 10000 ft-lb/in | Average value: 0.787 J/cm Grade Count:137 |
| 0.224238 - 5338.47 J/cm @Temperature -40.0 - -18.0 °C | 0.420090 - 10001.1 ft-lb/in @Temperature -40.0 - -0.400 °F | Average value: 1.67 J/cm Grade Count:24 | |
| Izod Impact, Unnotched | 0.300 - 5340 J/cm | 0.562 - 10000 ft-lb/in | Average value: 0.300 J/cm Grade Count:3 |
| 5338.47 - 5338.47 J/cm @Temperature -18.0 - -18.0 °C | 10001.1 - 10001.1 ft-lb/in @Temperature -0.400 - -0.400 °F | Grade Count:2 | |
| Izod Impact, Notched (ISO) | 11.0 - 80.1 kJ/m² | 5.23 - 38.1 ft-lb/in² | Average value: 38.4 kJ/m² Grade Count:11 |
| Charpy Impact Unnotched | 1.60 J/cm² - NB | 7.61 ft-lb/in² - NB | Average value: 1.60 J/cm² Grade Count:8 |
| Charpy Impact, Notched | 0.200 - 11.0 J/cm² | 0.952 - 52.4 ft-lb/in² | Average value: 2.79 J/cm² Grade Count:32 |
| Tensile Impact Strength | 34.0 - 349 kJ/m² | 16.2 - 166 ft-lb/in² | Average value: 198 kJ/m² Grade Count:14 |
| Falling Dart Impact | 31.2 - 176 J | 23.0 - 130 ft-lb | Average value: 125 J Grade Count:3 |
| Coefficient of Friction | 0.0270 - 0.300 | 0.0270 - 0.300 | Average value: 0.161 Grade Count:5 |
| Tensile Creep Modulus, 1 hour | 400 - 570 MPa | 58000 - 82700 psi | Average value: 473 MPa Grade Count:3 |
| Tensile Creep Modulus, 1000 hours | 270 - 400 MPa | 39200 - 58000 psi | Average value: 327 MPa Grade Count:3 |
| Tear Strength Test | 23.5 - 30.0 | 23.5 - 30.0 | Average value: 28.4 Grade Count:4 |
| Elmendorf Tear Strength, MD | 0.600 - 1.60 g/micron | 15.2 - 40.6 g/mil | Average value: 0.940 g/micron Grade Count:5 |
| Elmendorf Tear Strength, TD | 1.70 - 23.0 g/micron | 43.2 - 584 g/mil | Average value: 10.5 g/micron Grade Count:5 |
| Dart Drop | 1.50 - 2.00 g/micron | 38.1 - 50.8 g/mil | Average value: 1.67 g/micron Grade Count:4 |
| Film Tensile Strength at Break, MD | 35.6 - 55.0 MPa | 5160 - 7980 psi | Average value: 47.1 MPa Grade Count:5 |
| Film Tensile Strength at Break, TD | 28.0 - 50.0 MPa | 4060 - 7250 psi | Average value: 42.2 MPa Grade Count:5 |
| Tangent Modulus | 1170 - 1280 MPa | 170000 - 185000 psi | Average value: 1230 MPa Grade Count:5 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+6 - 1.00e+17 ohm-cm | 1.00e+6 - 1.00e+17 ohm-cm | Average value: 1.27e+16 ohm-cm Grade Count:17 |
| Surface Resistance | 100 - 1.00e+15 ohm | 100 - 1.00e+15 ohm | Average value: 1.58e+14 ohm Grade Count:15 |
| Dielectric Constant | 2.10 - 3.00 | 2.10 - 3.00 | Average value: 2.40 Grade Count:17 |
| Dielectric Strength | 18.7 - 150 kV/mm | 475 - 3810 kV/in | Average value: 53.2 kV/mm Grade Count:18 |
| Dissipation Factor | 0.0000400 - 0.00100 | 0.0000400 - 0.00100 | Average value: 0.000318 Grade Count:16 |
| Comparative Tracking Index | 600 V | 600 V | Average value: 600 V Grade Count:9 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 20.0 - 225 µm/m-°C | 11.1 - 125 µin/in-°F | Average value: 140 µm/m-°C Grade Count:27 |
| Thermal Conductivity | 0.288 - 0.480 W/m-K | 2.00 - 3.33 BTU-in/hr-ft²-°F | Average value: 0.396 W/m-K Grade Count:9 |
| Melting Point | 121 - 137 °C | 250 - 279 °F | Average value: 132 °C Grade Count:76 |
| Crystallization Temperature | 112 - 117 °C | 234 - 242 °F | Average value: 114 °C Grade Count:16 |
| Maximum Service Temperature, Air | 70.0 - 120 °C | 158 - 248 °F | Average value: 95.3 °C Grade Count:12 |
| Deflection Temperature at 0.46 MPa (66 psi) | 47.2 - 93.3 °C | 117 - 200 °F | Average value: 72.2 °C Grade Count:96 |
| Deflection Temperature at 1.8 MPa (264 psi) | 37.6 - 80.0 °C | 99.7 - 176 °F | Average value: 47.4 °C Grade Count:40 |
| Vicat Softening Point | 64.0 - 194 °C | 147 - 381 °F | Average value: 122 °C Grade Count:217 |
| Minimum Service Temperature, Air | -200 - -60.0 °C | -328 - -76.0 °F | Average value: -137 °C Grade Count:7 |
| Brittleness Temperature | -180 - -60.0 °C | -292 - -76.0 °F | Average value: -75.3 °C Grade Count:127 |
| Flammability, UL94 | HB | HB | Grade Count:24 |
| Oxygen Index | 17.0 - 20.0 % | 17.0 - 20.0 % | Average value: 19.1 % Grade Count:10 |
| Shrinkage | 0.960 - 3.50 % | 0.960 - 3.50 % | Average value: 1.77 % Grade Count:5 |
| Optical Properties | Metric | English | Comments |
| Yellow Index | 4.00 % | 4.00 % | Average value: 4.00 % Grade Count:14 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 82.2 - 274 °C | 180 - 525 °F | Average value: 211 °C Grade Count:17 |
| Nozzle Temperature | 160 - 246 °C | 320 - 475 °F | Average value: 234 °C Grade Count:13 |
| Melt Temperature | 130 - 280 °C | 266 - 536 °F | Average value: 215 °C Grade Count:49 |
| Mold Temperature | 10.0 - 65.6 °C | 50.0 - 150 °F | Average value: 31.8 °C Grade Count:13 |
| Drying Temperature | 37.8 - 80.0 °C | 100 - 176 °F | Average value: 53.9 °C Grade Count:3 |
| Dry Time | 1.00 - 3.00 hour | 1.00 - 3.00 hour | Average value: 2.00 hour Grade Count:3 |
| Injection Pressure | 2.76 - 103 MPa | 400 - 15000 psi | Average value: 62.4 MPa Grade Count:8 |