- 熔体流动速率 [g/10min]: 0.25
- 密度 [g/cm3]: 0.942
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.942 - 0.949 g/cc | 0.0340 - 0.0343 lb/in³ | Average value: 0.946 g/cc Grade Count:4 |
| Melt Flow | 0.250 - 0.400 g/10 min | 0.250 - 0.400 g/10 min | Average value: 0.313 g/10 min Grade Count:4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 59.0 - 70.0 | 59.0 - 70.0 | Average value: 63.0 Grade Count:3 |
| Film Tensile Strength at Yield, MD | 21.0 - 22.0 MPa | 3050 - 3190 psi | Average value: 21.3 MPa Grade Count:3 |
| Film Tensile Strength at Yield, TD | 22.0 - 24.0 MPa | 3190 - 3480 psi | Average value: 23.0 MPa Grade Count:3 |
| Film Elongation at Break, MD | 430 - 600 % | 430 - 600 % | Average value: 520 % Grade Count:3 |
| Film Elongation at Break, TD | 850 - 900 % | 850 - 900 % | Average value: 881 % Grade Count:3 |
| Secant Modulus, MD | 0.510 - 0.638 GPa | 74.0 - 92.5 ksi | Average value: 0.579 GPa Grade Count:3 |
| Secant Modulus, TD | 0.680 - 0.769 GPa | 98.6 - 112 ksi | Average value: 0.713 GPa Grade Count:3 |
| Izod Impact, Unnotched (ISO) | 19.8 - 26.2 kJ/m² | 9.42 - 12.5 ft-lb/in² | Average value: 23.4 kJ/m² Grade Count:4 |
| 17.9 - 23.0 kJ/m² @Temperature 0.000 - 0.000 °C | 8.52 - 10.9 ft-lb/in² @Temperature 32.0 - 32.0 °F | Average value: 20.4 kJ/m² Grade Count:4 | |
| Elmendorf Tear Strength, MD | 0.500 - 1.00 g/micron | 12.7 - 25.4 g/mil | Average value: 0.700 g/micron Grade Count:3 |
| Elmendorf Tear Strength, TD | 18.7 - 26.0 g/micron | 475 - 660 g/mil | Average value: 22.6 g/micron Grade Count:3 |
| Dart Drop | 0.600 - 2.70 g/micron | 15.2 - 68.6 g/mil | Average value: 1.54 g/micron Grade Count:3 |
| Film Tensile Strength at Break, MD | 35.0 - 54.0 MPa | 5080 - 7830 psi | Average value: 43.0 MPa Grade Count:3 |
| Film Tensile Strength at Break, TD | 33.0 - 39.0 MPa | 4790 - 5660 psi | Average value: 36.7 MPa Grade Count:3 |