- 熔体流动速率 [g/10min]: 0.04
- 密度 [g/cm3]: 0.933
- 吸水率 [%]: 0.01
- 缺口冲击强度: 0.2
- 拉伸强度 [MPa]: 13.0
- 断裂伸长率 [%]: 28.3
- 弯曲强度 [MPa]: 15.2
- 弯曲模量 [MPa]: 0.500
- 硬度: 80.0
- 热变形温度 [℃]: 62.0
- 脆化温度 [℃]: -118.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.933 - 1.27 g/cc | 0.0337 - 0.0459 lb/in³ | Average value: 0.958 g/cc Grade Count:129 |
| Volatiles | 0.0900 - 0.100 % | 0.0900 - 0.100 % | Average value: 0.0969 % Grade Count:14 |
| Apparent Bulk Density | 0.580 - 0.610 g/cc | 0.0210 - 0.0220 lb/in³ | Average value: 0.592 g/cc Grade Count:4 |
| Water Absorption | 0.0100 - 0.300 % | 0.0100 - 0.300 % | Average value: 0.111 % Grade Count:8 |
| Environmental Stress Crack Resistance | 10.0 - 10000 hour | 10.0 - 10000 hour | Average value: 1080 hour Grade Count:49 |
| 200 - 200 hour @Temperature 50.0 - 50.0 °C | 200 - 200 hour @Temperature 122 - 122 °F | Average value: 953 hour Grade Count:4 | |
| 139 - 139 hour @Temperature 50.0 - 50.0 °C | 139 - 139 hour @Temperature 122 - 122 °F | Average value: 953 hour Grade Count:3 | |
| 139 - 139 hour @Thickness 2.00 - 2.00 mm | 139 - 139 hour @Thickness 0.0787 - 0.0787 in | Average value: 953 hour Grade Count:3 | |
| Oxidative Induction Time (OIT) | 10.0 - 200 min | 10.0 - 200 min | Average value: 62.5 min Grade Count:4 |
| Linear Mold Shrinkage | 0.00500 - 0.00800 cm/cm | 0.00500 - 0.00800 in/in | Average value: 0.00675 cm/cm Grade Count:4 |
| Melt Flow | 0.0400 - 63.0 g/10 min | 0.0400 - 63.0 g/10 min | Average value: 4.00 g/10 min Grade Count:124 |
| Neck In | 5.00 - 11.1 cm | 1.97 - 4.37 in | Average value: 8.23 cm Grade Count:3 |
| Coating Weight | 6.00 - 10.4 g/m² | 3.75 - 6.50 lb/ream | Average value: 8.93 g/m² Grade Count:3 |
| Ash | 0.0400 - 0.0600 % | 0.0400 - 0.0600 % | Average value: 0.0553 % Grade Count:14 |
| Mechanical Properties | Metric | English | Comments |
| PENT | 30.0 - 100 hour | 30.0 - 100 hour | Average value: 76.7 hour Grade Count:3 |
| Hardness, Rockwell R | 80.0 - 112 | 80.0 - 112 | Average value: 90.7 Grade Count:3 |
| Hardness, Shore D | 55.0 - 70.0 | 55.0 - 70.0 | Average value: 63.0 Grade Count:53 |
| Tensile Strength, Ultimate | 15.2 - 45.0 MPa | 2200 - 6530 psi | Average value: 26.5 MPa Grade Count:55 |
| 11.0 - 25.0 MPa @Temperature -30.0 - 70.0 °C | 1600 - 3630 psi @Temperature -22.0 - 158 °F | Average value: 20.3 MPa Grade Count:1 | |
| Tensile Strength, Yield | 13.0 - 200 MPa | 1890 - 29000 psi | Average value: 26.3 MPa Grade Count:84 |
| 6.89476 - 30.0 MPa @Temperature -30.0 - 70.0 °C | 1000.00 - 4350 psi @Temperature -22.0 - 158 °F | Average value: 20.6 MPa Grade Count:1 | |
| Film Elongation at Break, MD | 400 - 600 % | 400 - 600 % | Average value: 500 % Grade Count:4 |
| Film Elongation at Break, TD | 450 - 650 % | 450 - 650 % | Average value: 550 % Grade Count:4 |
| Elongation at Break | 3.00 - 2200 % | 3.00 - 2200 % | Average value: 651 % Grade Count:99 |
| 200 - 500 % @Temperature -30.0 - 70.0 °C | 200 - 500 % @Temperature -22.0 - 158 °F | Average value: 367 % Grade Count:1 | |
| Elongation at Yield | 8.00 - 14.0 % | 8.00 - 14.0 % | Average value: 10.4 % Grade Count:9 |
| 4.00 - 9.00 % @Temperature -30.0 - 70.0 °C | 4.00 - 9.00 % @Temperature -22.0 - 158 °F | Average value: 5.67 % Grade Count:1 | |
| Modulus of Elasticity | 0.620 - 1.30 GPa | 89.9 - 189 ksi | Average value: 0.883 GPa Grade Count:9 |
| Flexural Yield Strength | 28.3 - 91.0 MPa | 4100 - 13200 psi | Average value: 62.5 MPa Grade Count:5 |
| Flexural Modulus | 0.500 - 4.83 GPa | 72.5 - 700 ksi | Average value: 1.19 GPa Grade Count:63 |
| Secant Modulus | 0.531 - 1.24 GPa | 77.0 - 180 ksi | Average value: 0.869 GPa Grade Count:6 |
| Izod Impact, Notched | 0.200 - 7.50 J/cm | 0.375 - 14.1 ft-lb/in | Average value: 2.22 J/cm Grade Count:27 |
| 0.700 - 1.10 J/cm @Temperature -40.0 - -40.0 °C | 1.31 - 2.06 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 0.900 J/cm Grade Count:2 | |
| Tensile Impact Strength | 80.0 - 480 kJ/m² | 38.1 - 228 ft-lb/in² | Average value: 243 kJ/m² Grade Count:7 |
| Tensile Impact | 68.3 - 152 J/cm | 128 - 285 ft-lb/in | Average value: 88.4 J/cm Grade Count:6 |
| Coefficient of Friction | 0.200 - 0.280 | 0.200 - 0.280 | Average value: 0.240 Grade Count:4 |
| Tear Strength Test | 17.0 - 29.4 | 17.0 - 29.4 | Average value: 21.6 Grade Count:11 |
| Elmendorf Tear Strength MD | 20.4 - 33.6 g | 20.4 - 33.6 g | Average value: 23.9 g Grade Count:4 |
| Elmendorf Tear Strength TD | 40.8 - 204 g | 40.8 - 204 g | Average value: 99.4 g Grade Count:4 |
| Film Tensile Strength at Break, MD | 45.0 - 55.0 MPa | 6530 - 7980 psi | Average value: 47.8 MPa Grade Count:4 |
| Film Tensile Strength at Break, TD | 40.0 - 46.0 MPa | 5800 - 6670 psi | Average value: 42.3 MPa Grade Count:4 |
| Hydrostatic Design Basis | 5.50 - 11.0 MPa | 798 - 1600 psi | Average value: 8.81 MPa Grade Count:3 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 10000 - 1.00e+20 ohm-cm | 10000 - 1.00e+20 ohm-cm | Average value: 5.48e+18 ohm-cm Grade Count:19 |
| Surface Resistance | 10000 - 1.00e+17 ohm | 10000 - 1.00e+17 ohm | Average value: 2.50e+16 ohm Grade Count:4 |
| Dielectric Constant | 2.05 - 2.50 | 2.05 - 2.50 | Average value: 2.33 Grade Count:14 |
| Dielectric Strength | 11.8 - 45.0 kV/mm | 300 - 1140 kV/in | Average value: 24.5 kV/mm Grade Count:11 |
| Dissipation Factor | 0.0000200 - 0.000500 | 0.0000200 - 0.000500 | Average value: 0.000152 Grade Count:12 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 34.2 - 200 µm/m-°C | 19.0 - 111 µin/in-°F | Average value: 123 µm/m-°C Grade Count:11 |
| Melting Point | 124 - 135 °C | 255 - 275 °F | Average value: 129 °C Grade Count:19 |
| Maximum Service Temperature, Air | 80.0 - 260 °C | 176 - 500 °F | Average value: 135 °C Grade Count:3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 62.0 - 143 °C | 144 - 290 °F | Average value: 85.9 °C Grade Count:19 |
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 - 127 °C | 111 - 260 °F | Average value: 82.7 °C Grade Count:8 |
| Vicat Softening Point | 80.0 - 131 °C | 176 - 268 °F | Average value: 122 °C Grade Count:47 |
| Brittleness Temperature | -118 - 76.0 °C | -180 - 169 °F | Average value: -79.3 °C Grade Count:48 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:4 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 180 - 240 °C | 356 - 464 °F | Average value: 211 °C Grade Count:5 |
| Feed Temperature | 149 - 163 °C | 300 - 325 °F | Average value: 156 °C Grade Count:7 |
| Adapter Temperature | 210 - 260 °C | 410 - 500 °F | Average value: 247 °C Grade Count:7 |
| Die Temperature | 210 - 260 °C | 410 - 500 °F | Average value: 247 °C Grade Count:7 |
| Melt Temperature | 124 - 321 °C | 255 - 610 °F | Average value: 216 °C Grade Count:35 |