- 熔体流动速率 [g/10min]: 1.7
- 密度 [g/cm3]: 0.941
- 缺口冲击强度: 2.29577
- 拉伸强度 [MPa]: 17.9
- 弯曲模量 [MPa]: 0.600
- 热变形温度 [℃]: 52.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.941 - 0.952 g/cc | 0.0340 - 0.0344 lb/in³ | Average value: 0.946 g/cc Grade Count:26 |
| Environmental Stress Crack Resistance | 8.00 - 1000 hour | 8.00 - 1000 hour | Average value: 373 hour Grade Count:19 |
| >= 1000 hour @Temperature 50.0 - 50.0 °C | >= 1000 hour @Temperature 122 - 122 °F | Average value: 1000 hour Grade Count:2 | |
| Melt Flow | 1.70 - 6.00 g/10 min | 1.70 - 6.00 g/10 min | Average value: 3.52 g/10 min Grade Count:26 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 64.0 - 67.0 | 64.0 - 67.0 | Average value: 65.3 Grade Count:9 |
| Tensile Strength, Yield | 17.9 - 26.6 MPa | 2600 - 3860 psi | Average value: 22.1 MPa Grade Count:30 |
| Elongation at Break | 350 - 700 % | 350 - 700 % | Average value: 517 % Grade Count:22 |
| Elongation at Yield | 12.0 - 20.0 % | 12.0 - 20.0 % | Average value: 18.4 % Grade Count:10 |
| Flexural Modulus | 0.600 - 1.15 GPa | 87.0 - 167 ksi | Average value: 0.875 GPa Grade Count:30 |
| Izod Impact, Notched | 2.29577 - 2.40255 J/cm @Temperature -40.0 - -40.0 °C | 4.30092 - 4.50096 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 2.32 J/cm Grade Count:4 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 126 - 133 °C | 259 - 271 °F | Average value: 131 °C Grade Count:16 |
| Deflection Temperature at 0.46 MPa (66 psi) | 52.0 - 142 °C | 126 - 288 °F | Average value: 76.3 °C Grade Count:21 |
| Deflection Temperature at 1.8 MPa (264 psi) | 41.0 - 99.0 °C | 106 - 210 °F | Average value: 53.7 °C Grade Count:20 |