- 熔体流动速率 [g/10min]: 0.1
- 密度 [g/cm3]: 0.994
- 缺口冲击强度: 0.21
- 拉伸强度 [MPa]: 15.0
- 断裂伸长率 [%]: 29.8
- 弯曲强度 [MPa]: 15.0
- 弯曲模量 [MPa]: 1.12
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.994 - 1.24 g/cc | 0.0359 - 0.0448 lb/in³ | Average value: 1.08 g/cc Grade Count:7 |
| Linear Mold Shrinkage | 0.00560 - 0.0140 cm/cm | 0.00560 - 0.0140 in/in | Average value: 0.00908 cm/cm Grade Count:5 |
| Melt Flow | 0.100 - 23.6 g/10 min | 0.100 - 23.6 g/10 min | Average value: 4.69 g/10 min Grade Count:6 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 15.0 - 23.1 MPa | 2180 - 3350 psi | Average value: 17.3 MPa Grade Count:4 |
| Tensile Strength, Yield | 15.0 - 33.9 MPa | 2180 - 4920 psi | Average value: 19.1 MPa Grade Count:6 |
| Elongation at Break | 0.790 - 15.0 % | 0.790 - 15.0 % | Average value: 7.06 % Grade Count:7 |
| Modulus of Elasticity | 1.70 - 4.86 GPa | 247 - 705 ksi | Average value: 3.21 GPa Grade Count:6 |
| Flexural Yield Strength | 29.8 - 43.0 MPa | 4320 - 6240 psi | Average value: 34.5 MPa Grade Count:6 |
| Flexural Modulus | 1.12 - 4.10 GPa | 163 - 595 ksi | Average value: 2.05 GPa Grade Count:6 |
| Izod Impact, Notched | 0.210 - 0.430 J/cm | 0.393 - 0.806 ft-lb/in | Average value: 0.310 J/cm Grade Count:4 |
| Izod Impact, Unnotched | 0.270 - 2.40 J/cm | 0.506 - 4.50 ft-lb/in | Average value: 1.11 J/cm Grade Count:5 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 36.0 - 99.0 µm/m-°C | 20.0 - 55.0 µin/in-°F | Average value: 64.3 µm/m-°C Grade Count:3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 43.0 - 62.0 °C | 109 - 144 °F | Average value: 50.4 °C Grade Count:5 |
| Flammability, UL94 | HB | HB | Grade Count:3 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 200 °C | 392 °F | Average value: 200 °C Grade Count:5 |