- 断裂伸长率 [%]: 22.8
- 弯曲模量 [MPa]: 0.772
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 0.945 g/cc | 0.945 g/cc | ASTM D792 | ||
| Water Absorption | <= 0.01 % | <= 0.01 % | Immersion, 24hr; ASTM D570(2) | ||
| Water Absorption at Saturation | <= 0.01 % | <= 0.01 % | Immersion; ASTM D570(2) | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 67 | 67 | ASTM D2240 | ||
| Tensile Strength | 33.1 MPa | 4800 psi | ASTM D638 | ||
| Elongation at Break | 250 % | 250 % | ASTM D638 | ||
| Tensile Modulus | 0.855 GPa | 124 ksi | ASTM D638 | ||
| Flexural Yield Strength | 22.8 MPa | 3300 psi | ASTM D790 | ||
| Flexural Modulus | 0.772 GPa | 112 ksi | ASTM D790 | ||
| Compressive Strength | 20.7 MPa | 3000 psi | 10% Def.; ASTM D695 | ||
| Compressive Modulus | 0.600 GPa | 87.0 ksi | ASTM D695 | ||
| Izod Impact, Notched | NB | NB | ASTM D256 Type A | ||
| Coefficient of Friction | 0.14 | 0.14 | Dry vs. Steel; QTM55007 | ||
| Sand Slurry | 8 | 8 | 1018 Steel = 100 | ||
| Limiting Pressure Velocity | 0.140 MPa-m/sec | 4000 psi-ft/min | 4:1 safety factor; QTM 55007 | ||
| Electrical Properties | Metric | English | Comments | ||
| Surface Resistivity per Square | 100000 - 1.00e+9 ohm | 100000 - 1.00e+9 ohm | ASTM D257 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 180 µm/m-°C @Temperature -40.0 - 149 °C | 100 µin/in-°F @Temperature -40.0 - 300 °F | ASTM E831 | ||
| Melting Point | 135 °C | 275 °F | Crystalline, Peak; ASTM D3418 | ||
| Maximum Service Temperature, Air | 82.2 °C | 180 °F | Long Term | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 46.7 °C | 116 °F | ASTM D648 | ||
| Flammability, UL94 | HB | HB | 1/8 inch (Estimated Rating) | ||
| Compliance Properties | Metric | English | Comments | ||
| 3A-Dairy | No | No | |||
| Canada AG | No | No | |||
| FDA | No | No | |||
| NSF | No | No | |||
| USDA | No | No | |||
| USP Class VI | No | No | |||
| Chemical Resistance Properties | Metric | English | Comments | ||
| Acids, Strong (pH 1-3) | Limited | Limited | |||
| Acids, Weak | Acceptable | Acceptable | |||
| Alcohols | Acceptable | Acceptable | |||
| Alkalies, Strong (pH 11-14) | Acceptable | Acceptable | |||
| Alkalies, Weak | Acceptable | Acceptable | |||
| Chlorinated Solvents | Acceptable | Acceptable | |||
| Conductive / Static Dissipative | Yes | Yes | |||
| Continuous Sunlight | Limited | Limited | |||
| Hot Water / Steam | Limited | Limited | |||
| Hydrocarbons - Aliphatic | Acceptable | Acceptable | |||
| Hydrocarbons - Aromatic | Unacceptable | Unacceptable | |||
| Inorganic Salt Solutions | Acceptable | Acceptable | |||
| Ketones, Esters | Limited | Limited | |||
| Descriptive Properties | |||||
| Machinability | 3 | 1-10, 1=Easier to Machine | |||