- 熔体流动速率 [g/10min]: 5.0
- 密度 [g/cm3]: 1.0
- 缺口冲击强度: 0.534
- 拉伸强度 [MPa]: 30.0
- 弯曲模量 [MPa]: 1.700
- 硬度: 50.0
- 热变形温度 [℃]: 119.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.00 g/cc | 0.0361 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | MD; ASTM D955 |
| Melt Flow | 5.0 g/10 min | 5.0 g/10 min | ASTM D1238 |
| Ash | 10 % | 10 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 50 | 50 | ASTM D785 |
| Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM D638 |
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | ASTM D638 |
| Elongation at Break | 165 % | 165 % | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 2.050 GPa | 297.3 ksi | ASTM D638 |
| Flexural Strength | 29.0 MPa | 4210 psi | ASTM D790 |
| Flexural Modulus | 1.700 GPa | 246.5 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C | 246 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | |