- 熔体流动速率 [g/10min]: 11.0
- 密度 [g/cm3]: 0.944
- 拉伸强度 [MPa]: 22.0
- 弯曲模量 [MPa]: 0.760
- 脆化温度 [℃]: -75.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.944 g/cc | 0.0341 lb/in³ | ASTM D1505 | ||
| Melt Flow | 11 g/10 min | 11 g/10 min | Condition 190/2.16, HLMI; ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| PENT | >= 100 hour | >= 100 hour | Slow crack growth; ASTM F1473 | ||
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | 2 in/min, Type IV bar; ASTM D638 | ||
| Elongation at Break | 800 % | 800 % | 2 in/min, Type IV bar; ASTM D638 | ||
| Flexural Modulus | 0.760 GPa | 110 ksi | 2% Secant - 16:1 span:depth,0.5 in/min; ASTM D3350 | ||
| 0.960 GPa | 139 ksi | Tangent, 16:1 span:depth,0.5in/min; ASTM D790 | |||
| Hydrostatic Design Basis | 5.50 MPa | 798 psi | 60°C; ASTM D2837 | ||
| 11.0 MPa | 1600 psi | Room Temperature; ASTM D2837 | |||
| Thermal Properties | Metric | English | Comments | ||
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | Type A clamp, type 1 specimen; ASTM D746 | ||
| Descriptive Properties | |||||
| Minimum Required Strength | 8 MPa | ISO 9080 | |||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.