- 熔体流动速率 [g/10min]: 9.0
- 拉伸强度 [MPa]: 24.0
- 弯曲模量 [MPa]: 0.830
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.948 g/cc | 0.948 g/cc | ASTM D1505 |
| Melt Flow | 9.0 g/10 min @Load 21.6 kg, Temperature 190 °C | 9.0 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| PENT | >= 500 hour | >= 500 hour | ASTM F1473 |
| Tensile Strength, Yield | >= 24.0 MPa | >= 3480 psi | 2 in/min, Type IV bar; ASTM D638 |
| Elongation at Break | >= 700 % | >= 700 % | 2 in/min, Type IV bar; ASTM D638 |
| Flexural Modulus | 0.830 GPa | 120 ksi | 2% Secant; ASTM D790 |
| Hydrostatic Design Basis | 6.90 MPa @Temperature 60.0 °C | 1000 psi @Temperature 140 °F | ASTM D2837 |
| 11.0 MPa @Temperature 23.0 °C | 1600 psi @Temperature 73.4 °F | ASTM D2837 | |