- 熔体流动速率 [g/10min]: 0.1
- 拉伸强度 [MPa]: 27.0
- 弯曲模量 [MPa]: 0.965
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.953 g/cc | 0.953 g/cc | ASTM D1505 |
| ESCR 100% Igepal® | >= 600 hour | >= 600 hour | Condition C, f20; ASTM D1693 |
| ESCR 10% Igepal® | >= 1000 hour | >= 1000 hour | Condition B, F50; ASTM D1693 |
| Oxidative Induction Time (OIT) | >= 100 min @Temperature 200 °C | >= 100 min @Temperature 392 °F | ASTM D3895 |
| Melt Flow | 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.10 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| 18 g/10 min @Load 21.6 kg, Temperature 190 °C | 18 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | >= 27.0 MPa | >= 3920 psi | 2 in/min, Type IV bar; ASTM D638 |
| Elongation at Break | 600 % | 600 % | 2 in/min, Type IV bar; ASTM D638 |
| Flexural Modulus | 0.965 GPa | 140 ksi | 2% Secant; ASTM D790 |
| Tensile Load, Notched Constant | >= 175 hour | >= 175 hour | Ligament Stress, Average of five; ASTM F2136 |