- 熔体流动速率 [g/10min]: 8.0
- 密度 [g/cm3]: 0.961
- 拉伸强度 [MPa]: 25.5
- 弯曲模量 [MPa]: 0.965
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.961 g/cc | 0.0347 lb/in³ | ASTM D-1505 | ||
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min | HLMI, 190/21.6; ASTM D-1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| PENT | >= 5000 hour | >= 5000 hour | slow crack growth; ASTM F-1473 | ||
| Tensile Strength, Yield | 25.5 MPa | 3700 psi | 2 in/min, Type IV bar; ASTM D-638 | ||
| Elongation at Break | >= 700 % | >= 700 % | 2 in/min, Type IV bar; ASTM D-638 | ||
| Flexural Modulus | 0.965 GPa | 140 ksi | 2% Secant - 16:1 span:depth, 0.5 in/min; ASTM D-790 | ||
| Hydrostatic Design Basis | 11.0 MPa | 1600 psi | Room Temperature; ASTM D-2837 | ||
| Descriptive Properties | |||||
| Hydrostatic Design Basis @ 140°F MPa | 6.9 | ASTM D-2837 | |||
| Hydrostatic Strength, hour | >10000 | at 5.0MPa, 80°C; ISO 1167 | |||
| >400 | at 12.4Mpa, 20°C; ISO 1167 | ||||
| >8000 | at 5.5MPa, 80°C; ISO 1167 | ||||
| Notched Pipe Test @ 4.6 MPa hour | 500 | ISO 13479 | |||
| Rapid Crack Propagation bar | >10 | S4 crit. pressure, -15°C; ISO 13477 | |||
| 30 | Full Scale Test, 0°C; ISO 13478 | ||||
| Required Minimum Strength MPa | 10 | ISO 9080 | |||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.