- 熔体流动速率 [g/10min]: 0.11
- 密度 [g/cm3]: 0.944
- 拉伸强度 [MPa]: 22.0
- 弯曲强度 [MPa]: 34.0
- 弯曲模量 [MPa]: 0.960
- 脆化温度 [℃]: -90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.944 g/cc | 0.0341 lb/in³ | ASTM D1505 |
| Environmental Stress Crack Resistance | >= 1000 hour @Temperature 50.0 °C | >= 1000 hour @Temperature 122 °F | Conditions A, B and C; ASTM D 1693 |
| Melt Flow | 0.11 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.11 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| High Load Melt Index | 10 g/10 min @Load 21.6 kg, Temperature 190 °C | 10 g/10 min @Load 47.6 lb, Temperature 374 °F | High Load; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 34.0 MPa | 4930 psi | ASTM D638 Type IV |
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | ASTM D638 Type IV |
| Elongation at Break | >= 500 % | >= 500 % | ASTM D638 Type IV |
| Flexural Modulus | 0.960 GPa | 139 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -90.0 °C | <= -130 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 193 - 216 °C | 379 - 421 °F | adequate mixing to achieve good dispersion |