- 密度 [g/cm3]: 0.939
- 拉伸强度 [MPa]: 26.2
- 弯曲模量 [MPa]: 0.689
- 脆化温度 [℃]: -100.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.939 g/cc | 0.0339 lb/in³ | natural resin; ASTM D792 |
| Environmental Stress Crack Resistance | >= 2000 hour | >= 2000 hour | Fo; Compression molded parts prepared according to ASTM D 1928, condition A.; ASTM D1693 |
| High Load Melt Index | 20 g/10 min @Load 21.6 kg, Temperature 190 °C | 20 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 |
| Melt Index of Compound | 0.15 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.15 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 55 | 55 | Compression molded parts prepared according to ASTM D 1928 Procedure C.; ASTM D2240 |
| Tensile Strength at Break | 30.0 MPa | 4350 psi | Compression molded parts prepared according to ASTM D 1928 Procedure C.; ASTM D638 |
| Tensile Strength, Yield | 26.2 MPa | 3800 psi | Compression molded parts prepared according to ASTM D 1928 Procedure C.; ASTM D638 |
| Elongation at Break | >= 800 % | >= 800 % | Compression molded parts prepared according to ASTM D 1928 Procedure C.; ASTM D638 |
| Flexural Modulus | 0.689 GPa | 100 ksi | Compression molded parts prepared according to ASTM D 1928, method 1, procedure B.; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 125 °C | 257 °F | Dow Method (DSC) |
| Vicat Softening Point | 116 °C | 241 °F | ASTM D1525 |
| Brittleness Temperature | <= -100 °C | <= -148 °F | Compression molded parts prepared according to ASTM D 1928, procedure A.; ASTM D746 |