- 熔体流动速率 [g/10min]: 20.0
- 密度 [g/cm3]: 0.952
- 拉伸强度 [MPa]: 24.8
- 弯曲模量 [MPa]: 0.965
- 脆化温度 [℃]: -70.6
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in³ | ASTM D1505 |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 190 °C | 20 g/10 min @Load 4.76 lb, Temperature 374 °F | Procedure A Condition E; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 24.8 MPa | 3600 psi | Type IV bar at chs 2 in per min; ASTM D638 |
| Elongation at Break | 300 % | 300 % | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 0.965 - 1.24 GPa | 140 - 180 ksi | Test Method I, Procedure B (chs speed 0.05 in/min); ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 122 °C | 252 °F | ASTM D1525 |
| Brittleness Temperature | <= -70.6 °C | <= -95.0 °F | ASTM D1525 |