- 熔体流动速率 [g/10min]: 23.0
- 密度 [g/cm3]: 0.953
- 弯曲模量 [MPa]: 1.03
- 脆化温度 [℃]: -113.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.953 g/cc | 0.0344 lb/in³ | ASTM D1505 |
| Melt Flow | 23 - 27 g/10 min @Load 2.16 kg, Temperature 230 °C | 23 - 27 g/10 min @Load 4.76 lb, Temperature 446 °F | Procedure A Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 25.9 MPa | 3750 psi | chs 2 in/min; ASTM D638 |
| Elongation at Break | 250 % | 250 % | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 1.03 GPa | 150 ksi | Test Method I, Procedure B (chs speed 0.05 in/min); ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -113 °C | <= -171 °F | ASTM D746 |