- 熔体流动速率 [g/10min]: 40.0
- 密度 [g/cm3]: 0.952
- 弯曲模量 [MPa]: 0.965
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in³ | ASTM D1505 |
| Melt Flow | 40 g/10 min @Load 2.16 kg, Temperature 190 °C | 40 g/10 min @Load 4.76 lb, Temperature 374 °F | Procedure A Condition E; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 23.4 MPa | 3400 psi | chs 2 in/min; ASTM D638 |
| Elongation at Break | 100 % | 100 % | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 0.965 GPa | 140 ksi | Test Method I, Procedure B (chs speed 0.05 in/min); ASTM D790 |