- 密度 [g/cm3]: 0.951
- 弯曲模量 [MPa]: 1.17
- 热变形温度 [℃]: 73.0
- 脆化温度 [℃]: -76.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.951 g/cc | 0.0344 lb/in³ | ASTM D1505 |
| High Load Melt Index | 11.5 g/10 min @Load 21.6 kg, Temperature 190 °C | 11.5 g/10 min @Load 47.6 lb, Temperature 374 °F | Procedure A Condition F (HLMI); ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 26.5 MPa | 3840 psi | chs 2 in/min; ASTM D638 |
| Elongation at Break | >= 600 % | >= 600 % | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 1.17 GPa | 170 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 73.0 °C | 163 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.1 °C | <= -105 °F | ASTM D746 |