- 密度 [g/cm3]: 0.958
- 拉伸强度 [MPa]: 27.6
- 弯曲模量 [MPa]: 1.10
- 脆化温度 [℃]: -70.6
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.958 g/cc | 0.0346 lb/in³ | ASTM D1505 |
| ESCR 100% Igepal® | 20 hour | 20 hour | Condition A; ASTM D1693 |
| High Load Melt Index | 0.96 g/10 min @Load 21.6 kg, Temperature 190 °C | 0.96 g/10 min @Load 47.6 lb, Temperature 374 °F | Procedure A Condition F (HLMI); ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 67 | 67 | ASTM D2240 |
| Tensile Strength, Yield | 27.6 MPa | 4000 psi | 2 in per min; ASTM D638 |
| Elongation at Break | 1200 % | 1200 % | |
| Flexural Modulus | 1.10 GPa | 160 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -70.6 °C | <= -95.0 °F | ASTM D746 |