- 熔体流动速率 [g/10min]: 0.25
- 密度 [g/cm3]: 0.963
- 拉伸强度 [MPa]: 31.7
- 弯曲模量 [MPa]: 1.62
- 脆化温度 [℃]: -76.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.963 g/cc | 0.0348 lb/in³ | ASTM D4883 |
| ESCR 100% Igepal® | 20 hour | 20 hour | ASTM D1693 Condition B |
| Melt Flow | 0.25 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.25 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 31.7 MPa | 4600 psi | ASTM D638 |
| Elongation at Break | 450 % | 450 % | ASTM D638 |
| Flexural Modulus | 1.62 GPa | 235 ksi | Method1, Procedure A (1"x3"x0.125"), Tangent calculation; ASTM D790 |
| Tensile Impact Strength | 147 kJ/m² | 70.0 ft-lb/in² | ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 127 °C | 260 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.1 °C | <= -105 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 191 °C | 375 °F | |