- 熔体流动速率 [g/10min]: 8.0
- 密度 [g/cm3]: 0.965
- 缺口冲击强度: 0.769
- 拉伸强度 [MPa]: 28.1
- 弯曲模量 [MPa]: 1.185
- 热变形温度 [℃]: 71.0
- 脆化温度 [℃]: -70.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.965 g/cc | 0.0349 lb/in³ | ASTM D4883 | ||
| Environmental Stress Crack Resistance | <= 3.0 hour | <= 3.0 hour | Cond. B, 10%; ASTM D1693 | ||
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 8.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 28.1 MPa | 4070 psi | ASTM D638 | ||
| Elongation at Break | 48 % | 48 % | ASTM D638 | ||
| Flexural Modulus | 1.185 GPa | 171.8 ksi | 1% Secant; ASTM D790 | ||
| Izod Impact, Notched | 0.769 J/cm @Temperature -40.0 °C | 1.44 ft-lb/in @Temperature -40.0 °F | ASTM D256 | ||
| Tensile Impact Strength | 311.8 kJ/m² | 148.5 ft-lb/in² | -40°C; ASTM D1822 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 136 °C | 277 °F | ASTM D3418 | ||
| Crystallization Temperature | 116 °C | 241 °F | ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 71.0 °C | 160 °F | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | ASTM D648 | ||
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 | ||
| Descriptive Properties | |||||
| Features | Standard Processing Antioxidants Stabilizer | ||||
| Form | Pellet | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.