- 熔体流动速率 [g/10min]: 0.42
- 密度 [g/cm3]: 0.959
- 拉伸强度 [MPa]: 28.6
- 弯曲模量 [MPa]: 1.03
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.959 g/cc | 0.0346 lb/in³ | ASTM D 792 |
| Melt Flow | 0.42 g/10 min @Load 2.16 kg | 0.42 g/10 min @Load 4.76 lb | ASTM D 1238 |
| 1.6 g/10 min @Load 5.00 kg | 1.6 g/10 min @Load 11.0 lb | ASTM D 1238 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 28.6 MPa | 4150 psi | ASTM D 638 type IV |
| Elongation at Break | >= 750 % | >= 750 % | ASTM D 638, type IV |
| Flexural Modulus | 1.03 GPa | 150 ksi | ASTM D 790 |
| Secant Modulus, MD | 1.10 GPa | 160 ksi | ASTM D 882 A |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 129 °C | 265 °F | ASTM D3417 |