- 熔体流动速率 [g/10min]: 3.8
- 密度 [g/cm3]: 0.932
- 拉伸强度 [MPa]: 14.4
- 弯曲模量 [MPa]: 0.520
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.932 g/cc | 0.0337 lb/in³ | ASTM D792 |
| Environmental Stress Crack Resistance | >= 400 hour | >= 400 hour | F50, Condition A, ASTM D1693, 100% Igepal |
| Melt Flow | 3.8 g/10 min @Load 2.16 kg, Temperature 190 °C | 3.8 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 56 | 56 | ASTM D2240 |
| Tensile Strength, Yield | 14.4 MPa | 2090 psi | ASTM D638 |
| Elongation at Break | 900 % | 900 % | ASTM D638 |
| Flexural Modulus | 0.520 GPa | 75.4 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 108 °C | 226 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 170 - 215 °C | 338 - 419 °F | |