- 熔体流动速率 [g/10min]: 1.8
- 密度 [g/cm3]: 0.936
- 脆化温度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.936 g/cc | 0.0338 lb/in³ | ASTM D792 |
| Melt Flow | 1.8 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.8 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 17.0 MPa | 2470 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 18.0 MPa | 2610 psi | ASTM D882 |
| Film Elongation at Break, MD | 750 % | 750 % | ASTM D882 |
| Film Elongation at Break, TD | 950 % | 950 % | ASTM D882 |
| Secant Modulus, MD | 0.340 GPa | 49.3 ksi | ASTM D882 |
| Secant Modulus, TD | 0.370 GPa | 53.7 ksi | ASTM D882 |
| Coefficient of Friction | >= 0.50 | >= 0.50 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 1.00 g/micron | 25.4 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 5.00 g/micron | 127 g/mil | ASTM D1922 |
| Dart Drop | 1.00 g/micron | 25.4 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 42.0 MPa | 6090 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 38.0 MPa | 5510 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 111 °C | 232 °F | ASTM D1525 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D696 |
| Optical Properties | Metric | English | Comments |
| Haze | 15 % @Thickness 0.0250 mm | 15 % @Thickness 0.000984 in | ASTM D1003 |
| Gloss | 58 % | 58 % | 45°; 1 mil; ASTM D1894 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 225 - 235 °C | 437 - 455 °F | |