- 熔体流动速率 [g/10min]: 9.0
- 密度 [g/cm3]: 1.78
- 拉伸强度 [MPa]: 55.0
- 热变形温度 [℃]: 130.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.78 g/cc | 0.0643 lb/in³ | |
| Water Absorption | 0.00 % | 0.00 % | |
| Melt Flow | 9.0 g/10 min | 9.0 g/10 min | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 8.0 % | 8.0 % | |
| Modulus of Elasticity | 2.10 GPa | 305 ksi | |
| Charpy Impact Unnotched | 28.0 J/cm² | 133 ft-lb/in² | |
| 22.0 J/cm² @Temperature -30.0 °C | 105 ft-lb/in² @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 1.70 J/cm² | 8.09 ft-lb/in² | |
| 0.900 J/cm² @Temperature -30.0 °C | 4.28 ft-lb/in² @Temperature -22.0 °F | ||
| Tensile Impact Strength | 160 kJ/m² | 76.1 ft-lb/in² | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 2.00e+13 ohm-cm | 2.00e+13 ohm-cm | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Constant | 8.0 @Frequency 1e+6 Hz | 8.0 @Frequency 1e+6 Hz | |
| 10 @Frequency 100 Hz | 10 @Frequency 100 Hz | ||
| Dielectric Strength | 21.0 kV/mm | 533 kV/in | |
| Dissipation Factor | 0.032 @Frequency 100 Hz | 0.032 @Frequency 100 Hz | |
| 0.25 @Frequency 1e+6 Hz | 0.25 @Frequency 1e+6 Hz | ||
| Comparative Tracking Index | 250 V | 250 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 100 µm/m-°C @Temperature 20.0 °C | 55.6 µin/in-°F @Temperature 68.0 °F | in flow direction |
| CTE, linear, Transverse to Flow | 100 µm/m-°C @Temperature 20.0 °C | 55.6 µin/in-°F @Temperature 68.0 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | |
| Vicat Softening Point | 166 °C | 331 °F | 50°C/hr/50 N |
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | |